Kinou-96 Copper alloy (cu-9ni-6sn c72700)
1
| Hōʻailona | Ni | Sn | Mn | Pb | Zn | Fe | P | Palau | Cu |
| C72700 | 8.5-9.5 | 5.5-6.5 | 0,05-0.3 | ≤ «.03 | ≤0.15 | ≤ «.05 | ≤ «.05 | Ç0.5 | Hanau |
2.ʻO nā waiwai pilikino o C72700
| Huakai | 8.9 | (g / cm3) |
| Malting Point | 968578 | (℃) |
| ʻO ka hōʻike hōʻike hōʻike | 17.25 | (X10-6/ ℃) 20-200 ℃ |
| Elastic Modulus | 120 | (GPA) |
| Nā pale kaua uila ma 20 ℃ |
| μω * cm |
| Quetch | ≤19.5 |
|
| Hoʻonui nui | ≤15 |
|
| ʻO ka hana uila (ʻo iacs,%) |
| (% Iac) |
| ≥9 |
| |
| ʻO ka paʻakikī o ka paʻakikī (3 mau hola) | ≥12 |
|
| Kahuawa Model | 50 | (GPA) |
| Ka lahui lahilahi ma 20 ℃ | 53.6 | (W / mk) |
| Ke hoʻomau nei i ka ikaika | 450 | (MPA) |
3.ʻO nā waiwai hana / moku'āina o C72700
1) nā huahana i kālaiʻia
| Moku'āina | Hālulu | Ikaika ikaika | Ka ikaika | ELEDION | Ke kū nei * | Paʻakikī, elasticity a me nā bending subigne waiwai (MPA) | ||
| HV | RM (MPA) | Rp 0.2 (MPA) | A50mm (%) | Longitidinal // | Transiverin⊥ | Longitidinal // | Transiverin⊥ | |
| Queech | ||||||||
| TB | 90-125 | 420-500 | ≥200 | ≥30 | 0.2 | 0.2 | 302 | 220 |
| ʻO Quenching / Cold Rolling | ||||||||
| Td1 | 140-180 | 460-560 | ≥300 | ≥15 | 0.2 | 0.2 | 216 | 359 |
| TD2 | 160-200 | 540-640 | ≥400 | ≥10 | 0.2 | 0.2 | 275 | 390 |
| TD3 | 200-240 | 620-720 | ≥550 | ≥3 | 0,5 | 0,5 | 444 | 523 |
| Td4 | 220-260 | 700-820 | ≥600 | ≈1 | 2 | 1 | 467 | 568 |
| TDX | Tack320 | ≥680 | ≥650 | ≈1 | 10 | 2 | 472 | 613 |
| ʻO Quenching / hōʻoia i ka wela wela | ||||||||
| TF | 230-270 | 740-860 | ≥510 | ≥10 | 0,5 | 0,5 | 566 | 634 |
| Quenching / Cold Rolling / Ka Hoʻokele Ho'ōla Kūʻai Kūʻai | ||||||||
| Th1 | 270-310 | 850-950 | ≥650 | ≥8 | 0,5 | 0,5 | 684 | 724 |
| Th2 | 290-320 | 880-980 | ≥720 | ≥8 | 1 | 1 | 730 | 770 |
| K3 | 310-340 | 950-1050 | ≥800 | ≥4 | 1 | 1 | 829 | ≥840 |
| Kōa | 320-360 | 1000-1100 | ≥900 | ≈UU ≈3 | 2 | 2 | ≥830 | ≥840 |
| Thx | Ç390 | ≥1050 | ≥950 | ≈1 | / | / | ≥830 | ≥840 |
| *: E like me Dina 5011 (25/10/85), e kau ana i ka nui o ka radius e hoʻoholo ai i ka mānoanoa | ||||||||
2) Nā huahana Drawn
| Moku'āina | Hālulu | Ikaika ikaika | Ka ikaika | ELEDION | ʻO ka hoʻomaʻamaʻaʻana |
| HV | RM (MPA) | Rp 0.2 (MPA) | A50mm (%) | Z% | |
| Queech | |||||
| TB | ≤_8 | 400-500 | ≥200 | ≥30 | ≥80 |
| ʻO Quenching / Cold Rolling | |||||
| Td1 | 150-180 | 500-580 | ≥300 | ≥10 | ≥75 |
| TD2 | 180-230 | 550-720 | ≥500 | ≥3 | ≥70 |
| TD3 | 220-260 | 700-800 | ≥600 | ≥2 | ≥65 |
| Td4 | 230-300 | 780 .880 | ≥700 | ≥1.5 | ≥60 |
| TDX | 250-320 | 880-1000 | ≥800 | ≥0.1 | ≥50 |
|
|
|
|
|
|
|
| Moku'āina | HV | RM (MPA) | Rp 0.2 (MPA) | A50mm (%) | Z% |
| ʻO Quenching / hōʻoia i ka wela wela | |||||
| TF | ≤260 | 770-870 | ≥500 | ≥20 | ≥40 |
| Quenching / Cold Rolling / Ka Hoʻokele Ho'ōla Kūʻai Kūʻai | |||||
| Th1 | 260-300 | 870-970 | ≥700 | ≥13 | ≥30 |
| Th2 | 290-310 | 930-1030 | ≥800 | ≥8 | ≥30 |
| K3 | 310-330 | 1000-1100 | ≥900 | ≥5 | ≥30 |
| Kōa | 330-360 | 1100-1200 | ≥1000 | ≥2 | ≥30 |
| Thx | ≥,5050 | 1175-1300 | ≥1100 | ≥0.5 | ≥30 |
4.ʻO kaʻaeʻana o ke koʻokoʻo a me ke kelepona o C72700
| ʻAno | Olemela | ʻO kaʻaeʻana o ka diameter | Ka pololei o ka pololei | |||
| loko | mm | loko | mm | loko | mm | |
| Nā hāmeʻa | 0.2-0.39 | 6.35-9.9 | +/- 0.002 | +/ 685 | Long = 10FT, hoʻokaʻawale <0.25 mau iniha | Long = 3048mm, hoʻolaʻa <6.35mm |
| 0.4-0.74 | 10-18.9 | + 0.005 / -0 | + 0.13 / -0 | |||
| Kāla Rulu | 0.75-1.6 | 19-40.9 | +202 / + 0 0 0.08 | + 0.5 / + 2.0 | Long = 10FT, hoʻokaʻawale <0.5 mau iniha | Long = 3048mm, ka haʻaleleʻana <12mm |
| 1.61-2.75 | 41- | + 0.02 / + 0.10 | + 0.02 / + 0.10 | |||
| 2.76-3.25 | 70.1-82 | + 0.02 / + 0.145 | + 0.02 / + 0.145 | |||
| 3.26-6.00 | 83-152.4 | + 0.02 / + 0.187 | + 0.02 / + 0.187 | |||
| <0.4 | <10 | +/- 0.002 | +/ 685 |
|
| |
5.ʻO ka noi o C72700
Ke kiʻi nei i ke koho balota Boplium
Hoʻohanaʻia ia no nā aniani, nā uila, electromechanincial, nā mea uila, nā mea hoʻopili, nā hale kūʻai hale, nā mea kūʻai aku